The Effect of Rare Earth Dopants in Crystal Structure of Bi-2212 Superconductor

Bi2Sr2CaCu2O8+? samples have been successfully synthesized by doping rare earth (RE) variations using wet-mixing method. Samples calcined at 600oC for 3 hours and sintered at 850oC for 10 hours. The purpose of research is to determine the effect of the RE dopant on the microscopic structure of BSCRECO superconductors. Therefore, the research was conducted characterization by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscope (SEM). Measurements with XRD could be carried out and crystal system of Bi2Sr2CaCu2O8+? with rare earth (RE) dopants could be determined clearly. Generally, crystallization has occurred very well demonstrated by the diffraction peaks are sharp, which is dominated by the emergence of Bi-2212 phase. Search match results of XRD spectrum showed Bi2Sr2CuOx (2201) and Ca2CuO3 (21) as an impurity phase with small intensity. Also, that is showing volume fraction from 85 to 92% and orthorombic value for all samples from 5 to 7%. The effect of RE dopants resulted a shift angle 2? and changes in the volume of the unit cells of each sample. The value of the unit cell volume of the largest to smallest is BS(CN)CO, BS(CNG)CO, BS(CNEG)CO, BS(CNE)CO, BS(CG)CO, BS(CEG)CO and BS(CE)CO. Measurement with FTIR showed the bending vibration absorption by CO32- in the wavelength range between 1500 and 1520 cm-1, vibration of M-O between 420 and 650 cm-1, the complex formation of BSCCO in the wavelength range between 1690 and 1700 cm-1. Measurement with SEM showed rod shape with particle size in hundreds nanometer.