The Effect of UVC Irradiation on the Mechanical Properties of Chitosan Membrane in Sterilization Process

The present study, we report about the effect of UVC irradiation on the mechanical properties of chitosan membrane in the sterilization process. The membrane used was chitosan membrane 2% which prepared by a casting method using chitosan as matrix and acetic acid 1% as a solvent. The UVC source used was germicidal ultraviolet (UVG) which widely used for sterilization purposes. Variation doses were done by the varying time of irradiation, e.g. 5 min, 15 min, 30 min, and 60 min. Those samples are named as S1, S2, S3, and S4, respectively. Chitosan membrane before irradiation namely S0 also used for comparative study. The effect of UVC irradiation on the mechanical properties of membranes has been examined by different techniques including FTIR, DMA, and the water uptake capability. The results showed that ultimate tensile strength (UTS) and moduli of elasticity (E) were increased by increasing the irradiation time. From FTIR analysis obtained that no new molecules were formed in irradiated membranes. The water uptakes capability of the membranes after irradiation was smaller compared with before irradiation, and among the irradiated membranes, the water uptake capabilities were increased by increasing the exposure time. These observations suggested that more care should be taken during the sterilization process and outdoor used of the membrane. The other side, the UVC irradiation can improve the mechanical properties of the membranes.